MECHANICAL TESTING | Mechanical Testing of Materials | Mechanical Testing of Metals | Mechanical Testing of Welds | Mechanical Testing Facilities | Load & Tensile Test | Mechanical Testing Machine


  • Tensile Test
A tensile test, also known as a tension test, tests a material’s strength. It’s a mechanical test where a pulling force is applied to a material from both sides until the sample changes its shape or breaks. It’s is a common and important test that provides a variety of information about the material being tested, including the elongation, yield point, tensile strength, and ultimate strength of the material. Tensile tests are commonly performed on substances such as metals, plastics, wood, and ceramics.
01-Electronic_Tensile_Testing_Machine-calculate tensile strength-yield strength-ultimate strength-break value-elongation-testing steels, iron, plastics and composite materials
Tensile testing systems use a number of different units of measurement. The International System of Units, or SI, recommends the use of either Pascals (Pa) or Newtons per square meter (N/m²) for describing tensile strength. In the United States, many engineers measure tensile strength in kilo-pound per square inch (KSI).
01-TensileStrength-tensile test-Calculate Ultimate tensile strength-tensile property testing of plastics, steel, iron-material strength calculate - pascals - newton per square meter
  • Tensile test with electronic extensometer
01-electronic_extensometer-calculate proof stress - youngs modulus values-material stress-acccepts load-extension value
This instrument is to be used on Tensile or Universal testing machines to find out Proof stress & Young’s modulus values. In case of many brittle materials such as high carbon steels, alloy steels, light aluminium & magnesium alloys, it is difficult to get yield values. For such materials stress corresponding to a certain allowable amount of plastic deformation is termed as proof stress say 0.1% or 0.2% proof stress. The measuring range is up to 5mm & resolution is 0.001mm.
01-mechanical_extensometer-tensile test calculation-universal testing machine-utm
  • Tensile testing at elevated temperature.
01-tensile test at elevated temperature-high temperature tensile test-specialist tensile test
High temperature tensile testing is a procedure to test the properties of a material at above room temperature. It will determine the following parameters:
  • Tensile strength (breaking strength)
  • Yield strength
  • Elongation
  • Reduction of area
Specialist testing, measurement and control equipment is required to perform this test.
The results of such a test will provide a good indication of the static load bearing capacity of the material and therefore establishes the suitability of a material for its intended purpose.
  • Tensile test on Tor steel Bars
01-tor-steel-bar-rods-TMT steel Bars-concrete technology-durable-corrosion resistant-engineering and construction
TOR steel is one of the best grade of steel used in concrete reinforced. It’s a kind of high adherence steel. Other types of steel are used for less resistance concrete. Thermo mechanically Treated (TMT) bars are a type of corrosion resistant steel reinforcing bar used in concrete construction.
  • Bend test on plates
01-bend test on steels- cold bars -cold bend testing for steels
A bend test is used to determine whether a specific piece of metal in question will break or fracture under pressure. This is important in the construction of any project using metal, otherwise the building or the item being made could collapse from the immense pressure exerted on it. Every piece of metal made cannot be tested, therefore certain pieces are tested and if they pass, the other pieces are made using the same process. The results of a bend test are reported differently depending on the type of material tested. There is no standard method for reporting the durability that applies to all materials, rather each group has its own set by which it is judged and compared to other metals in that group.
The bend test is essentially measuring a metal’s ductility. Ductility defines how easily a metal can bend without breaking. The higher the ductility of a metal, the more it can bend without breaking or becoming deformed from its original shape. This is important because certain metals must handle pressure without snapping yet still be ductile enough to bend slightly and not lose their support or shape. Copper and steel are two metals that have a high ductility and do well under pressure.
  • Bend test on pipes
01-bend test on pipes
Bending tests are carried out to ensure that a metal has sufficient ductility to stand bending without fracturing. A standard specimen is bent through a specified arc and in the case of strip, the direction of grain flow is noted and whether the bend is with or across the grain.
  • Bend Test on Tor steel
01-wire-rods-rebend test on steels
The purpose is to make certain the weld and the base metal are properly fused, and that the weld metal and the heat affected zone (HAZ) have appropriate mechanical properties
  • Re-Bend test on Tor steel
01-wire-rods-rebend test on steelsThe purpose of re-bend test is to measure the effect of strain ageing on steel. Strain ageing has embrittlement effect which takes place after cold deformation by diffusion of nitrogen in steel. Hence, there is limitation stated in some design codes to restrict the nitrogen content of steel to 0.012%.
  • Nick Break Test
01-nick break test-welding-fabrication-on sheetsThe NICK-BREAK TEST is useful for determining the internal quality of the weld metal. This test reveals various internal defects (if present), such as slag inclusions,  gas  pockets,  lack of  fusion,  and  oxidized  or burned metal. To accomplish the nick-break test for checking a butt weld, you must first flame-cut the test specimens from a sample weld.